Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.42 g/cm³ |
| melt mass-flow rate | | ISO1133 | 2.5 g/10min |
| Shrinkage rate | | ISO294-4 | 2.0 % |
| Water absorption rate | | ISO62 | 0.25 % |
| Humidity-Pellets | | ISO1110 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 82 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 3000 MPa |
| Tensile stress | | ISO527-2 | 71.0 MPa |
| Tensile strain | Break | ISO527-2 | 65 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 15 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+15 ohms |
| dielectric strength | | IEC60243-1 | 32 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO75-2/B | 160 °C |
| Heat distortion temperature | | ISO75-2/A | 110 °C |
| vicat | | ISO306 | 170 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.