Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.14 g/cm³ |
| Humidity | | ISO 15512/B | <0.25 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| Burning wire flammability index | | IEC 60695-2-12 | 750 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 3700 MPa |
| tensile strength | Break | ISO 527-2/50 | 90.0 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 4.7 % |
| Tensile strain | Break | ISO 527-2/50 | >15 % |
| Flexural modulus | | ISO 178 | 2600 MPa |
| bending strength | | ISO 178 | 110 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 2.5 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ISO 75-2/A | 80.0 °C |
| vicat | | ISO 306 | >230 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare