Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.08 g/cm³ |
| Water absorption rate | | ASTMD570 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 92 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-1 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| shear strength | | ASTMD732 | 57.2 MPa |
| Tensile modulus | | ASTMD638 | 2530 MPa |
| tensile strength | Ultimate | ASTMD638 | 57.2 MPa |
| elongation | Break | ASTMD638 | 23 % |
| Flexural modulus | | ASTMD790 | 2740 MPa |
| bending strength | Yield | ASTMD790 | 88.9 MPa |
| Compression Modulus | | ASTMD695 | 2180 MPa |
| compressive strength | | ASTMD695 | 91.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256A | 160 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTMD149 | 28 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 127 °C |
| Maximum operating temperature LongTerm, Air | | | 93 °C |
| Glass Transition Temperature | | ASTMD3418 | 140 °C |
| | ASTME831 | 6.4E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.