Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.36 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 1.0 % |
| Shrinkage rate | | ISO 294-4 | 0.20 % |
| Water absorption rate | | ISO 62 | 6.0 % |
| Water absorption rate | | ISO 62 | 1.6 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | IEC 60695-11-10, -20 | HB |
| Flammability level | | IEC 60695-11-10, -20 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 9950 Mpa |
| Tensile stress | | ISO 527-2 | 200 Mpa |
| Tensile strain | | ISO 527-2 | 3.6 % |
| Flexural modulus | | ISO 178 | 8400 Mpa |
| Bending stress | | ISO 178 | 250 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 9.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 65 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 81 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | -- ohms |
| Volume resistivity | | IEC 60093 | 1.0E+14 ohms·cm |
| dielectric strength | | IEC 60243-1 | 30 KV/mm |
| | IEC 60250 | 3.80 |
| | IEC 60250 | 3.50 |
| Dissipation Factor | | IEC 60250 | 9.0E-3 |
| Dissipation Factor | | IEC 60250 | 0.016 |
| CTI | | IEC 60112 | 500 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 260 °C |
| Heat distortion temperature | | ISO 75-2/A | 250 °C |
| Melting temperature 3 | | ISO 11357-3 | 260 °C |
| | ISO 11359-2 | 2.0E-5 cm/cm/°C |
| | ISO 11359-2 | 7.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.