PBT 1500G15 SAMYANG KOREA

Form：Granules | Grade：Injection grade

Properties:

Medium viscosity

Typical Applications:

Laptop caseAutomotive sectorPhone caseEngine parts

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Laptop case \| Automotive sector \| Phone case \| Engine parts
Properties:	Medium viscosity

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			玻纤增强
Other performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1/6＂英寸	UL -94	HB
Conductivity	10	ASTM D-150	3.2
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ASTM D-790	50000	kg/cm
Rockwell hardness		ASTM D-785	119	R scale
bending strength		ASTM D-790	1500	kg/cm
elongation	Break	ASTM D-638	7	%
Impact strength of cantilever beam gap	1/8＂英寸	ASTM D-256	1/8＂英寸	kg.cm/cm
tensile strength		ASTM D-638	1100	kg/cm
tensile strength	tensile strength	Yield	ASTM D638	108	Mpa
elongation	Break	ASTM D638	7.0	%
Bending modulus		ASTM D790	4900	Mpa
bending strength	Yield	ASTM D790	147	Mpa
Impact strength of cantilever beam gap		ASTM D256/ISO 179	7	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	7	%
tensile strength		ASTM D638/ISO 527	1100	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	119
Bending modulus		ASTM D790/ISO 178	50000	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	1500	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature			224	°C
Hot deformation temperature	4.6kg/cm	ASTM D-648	225	°C
Linear coefficient of thermal expansion		ASTM D-696	3	mm/mm/℃
Hot deformation temperature	18.6kg/cm	ASTM D-648	210	°C
Linear coefficient of thermal expansion	MD	ASTM D696	3E-05	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	225	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	210	°C
		Hot deformation temperature	HDT	ASTM D648/ISO 75	225	℃（℉）
		Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	210	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	3	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		ASTM D-570	0.08	%
melt mass-flow rate	250°C/5.0kg	ASTM D1238	85	g/10min
Shrinkage rate	MD	ASTM D955	0.20-1.2	%
Water absorption rate	23°C,24hr	ASTM D570	0.080	%
density		ASTM D792/ISO 1183	1.5
melt mass-flow rate		ASTM D1238/ISO 1133	60	g/10min
Water absorption rate		ASTM D570/ISO 62	0.08	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Arc resistance		ASTM D-495	150	sec
Dissipation factor	10	ASTM D-150	0.02
Volume resistivity	1016	ASTM D-257	10	Ω.cm
Dielectric strength		ASTM D-257	21	KV/mm
Volume resistivity		ASTM D257	1E+16	ohms·cm
Dielectric strength		ASTM D149	21	KV/mm
Dielectric constant		ASTM D150	3.20
Dissipation factor		ASTM D150	0.020
Arc resistance		ASTM D495	150	sec
Volume resistivity		ASTM D257/IEC 60093	1	Ω.cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	119

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.