PMMA V040 ARKEMA FRANCE

Form：Granules | Grade：Heat resistant grade

Properties:

wear resistantHigh mobilitytransparentHigh temperature resistanForming method: extrusionExcellent wear resistance

Typical Applications:

Electronic fieldElectrical field

Supplier(1)

Product Description

Certificates(1)

Datasheet

Alternative Model(10)

Product Description

Typical Applications:	Electronic field \| Electrical field
Properties:	wear resistant \| High mobility \| transparent \| High temperature resistan \| Forming method: extrusion \| Excellent wear resistance

Certificates

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	浸水24hrs后增重	ASTM D-570	0.3	%
melt mass-flow rate		ASTM D-1238	3.5	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	横跨比=16	ASTM D-790	1050(103)	Kgf/cm
Impact strength of cantilever beam gap	Izod 研磨Notched	ASTM D256	1.2(12.3)	kgf-cm/cm(J/m)
tensile strength	初级Strain速度0.1cm/cm/min	ASTM D-638	720(70)	Kgf/cm
Impact strength of cantilever beam gap	落锤(15.2×15.2×0.3cm重1.4kg半径0.64cm)	ASTM D256	14(1.4)	kg-cm(J)
Bending modulus		ASTM D-790	32000	Kgf/cm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Glass transition temperature	Tg		108	°C
Hot deformation temperature	2℃/min,18.6kgf/cm，Annealed	ASTM D-648	102	°C
Temperature range for use	与残余应力大小有关		85-102	°C
Vicat softening temperature	50℃/hr,5kg	ASTM D-1525，未退火	104	°C
Vicat softening temperature	Vicat softening temperature	50℃/hr,1kg	ASTM D-1525，未退火	111	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	(冷模/冷件),48hrs	ASTM D-935	0.2-0.6	%
Refractive index		ASTM D-542	1.49
density		ASTM D-792	1.19
Transmittance rate		ASTM D-1003	92	%
Rockwell hardness		ASTM D-758(M级)	97

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.