Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.17 g/cm³ |
| Shrinkage rate | | | 1.0 % |
| Shrinkage rate | | | 1.0 % |
| Water absorption rate | | ISO62 | 2.6 % |
| Moisture content | | ISO960 | <2000 ppm |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 775 °C |
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/1A | 6.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 5.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO527-2/5 | 35 % |
| Tensile modulus | | ISO527-2/5 | 3500 MPa |
| Tensile stress | | ISO527-2/5 | 70.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+13 ohms |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 165 °C |
| | ISO75-2/A | 70.0 °C |
| vicat | | ISO306/B | 170 °C |
| melting temperature | | ISO11357 | 223 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare