ABS 900 TORAY MALAYSIA

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforcedHigh impact resistance

Typical Applications:

household electrical appliancesElectronic and electrical components

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	household electrical appliances \| Electronic and electrical components
Properties:	Glass fiber reinforced \| High impact resistance

Certificates

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	Total,3000μm	ISO 13468	86.0	%
turbidity	3000μm	ISO 14782	2.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C,12.7mm	ASTM D256	140	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	160	J/m
Charpy Notched Impact Strength	23°C	ISO 179	12	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D638	41.0	Mpa
tensile strength	tensile strength	Yield,23°C	ISO 527-2	48.0	Mpa
elongation	Break	ASTM D638	40	%
Tensile strain	Break,23°C	ISO 527-2	15	%
Bending modulus		ASTM D790	1810	Mpa
Bending modulus	Bending modulus	23°C	ISO 178	1870	Mpa
bending strength	23°C	ISO 178	66.0	Mpa
bending strength	bending strength		ASTM D790	63.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	81.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	76.0	°C
Vicat softening temperature			90.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.08	g/cm³
density	density	23°C	ISO 1183	1.08	g/cm³
melt mass-flow rate	220°C/10.0kg	ISO 1133	18	g/10min
Shrinkage rate		Internal Method	0.40-0.60	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ASTM D785	108
Rockwell hardness	Rockwell hardness	R-Sale,23°C	ISO 2039-2	108

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.