PC+Polyester XYLEX™ FXY330DF resin

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Water absorption rate		ISO62	0.70 %
Water absorption rate	Water absorption rate		ISO62	0.27 %
density		ASTMD792,ISO1183	1.17 g/cm³
melt mass-flow rate		ASTMD1238	15 g/10min
Melt volume flow rate		ISO1133	13.0 cm³/10min
Shrinkage rate		内部方法	0.50到0.70 %
Shrinkage rate	Shrinkage rate		内部方法	0.40到0.60 %

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTMD638	1440 MPa
Tensile modulus	Tensile modulus		ISO527-2/1	1580 MPa
tensile strength		ASTMD638	47.0 MPa
Bending stress		ASTMD790	67.0 MPa
elongation		ASTMD638	5.0 %
	elongation	Yield	ISO527-2/50	>5.0 %
		elongation		ASTMD638	170 %
		elongation	elongation	Break	ISO527-2/50	>200 %
Flexural modulus		ASTMD790	1500 MPa
Flexural modulus	Flexural modulus		ISO178	1600 MPa
Bending stress		ISO178	77.0 MPa
tensile strength	Yield	ISO527-2/50	49.0 MPa
	tensile strength		ASTMD638	49.0 MPa
	tensile strength	tensile strength	Break	ISO527-2/50	50.0 MPa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO179/1eA	7.0 kJ/m²
Impact strength of cantilever beam gap		ASTMD256	55 J/m
	Impact strength of cantilever beam gap		ASTMD256	64 J/m
		Impact strength of cantilever beam gap		ASTMD256	70 J/m
			Impact strength of cantilever beam gap		ISO180/1A	4.0 kJ/m²
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO180/1A	7.0 kJ/m²
Dart impact equipped with measuring instruments		ASTMD3763	60.0 J

Thermal performance	Test Condition	Test Method	Test Result
vicat		ASTMD152511	90.0 °C
	vicat		ISO306/B50	92.0 °C
	vicat	vicat		ISO306/B120	93.0 °C
		ASTME831	8.9E-05 cm/cm/°C
			ISO11359-2	9E-05 cm/cm/°C
				ASTME831	9.4E-05 cm/cm/°C
Heat distortion temperature		ASTMD648	72.0 °C
Heat distortion temperature	Heat distortion temperature		ISO75-2/Af	78.0 °C
		ISO11359-2	9E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.