Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.96 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.080 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| shear strength | | ASTM D732 | 145 MPa |
| compressive strength | | ASTM D695 | 296 MPa |
| compressive strength | | ASTM D695 | 291 MPa |
| compressive strength | | ASTM D695 | >334 MPa |
| Tensile modulus | | | 17200 MPa |
| tensile strength | | ASTM D638 | 403 MPa |
| tensile strength | | ASTM D638 | 269 MPa |
| bending strength | | ASTM D790 | 585 MPa |
| bending strength | | ASTM D790 | 456 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 520 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 850 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 19 kV/mm |
| dielectric constant | | ASTM D150 | 5.04 |
| dielectric constant | | ASTM D150 | 4.79 |
| dielectric strength | | ASTM D149 | 80000 V |
| Dissipation Factor | | ASTM D150 | 5E-03 |
| Dissipation Factor | | ASTM D150 | 0.016 |
| arc resistance | | ASTM D495 | 126 sec |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 1 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 0 mm/min |
| Hot wire ignition (HWI) | | UL 746 | PLC 0 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | | 1E-05 cm/cm/°C |
| thermal conductivity | | | 0.29 W/m/K |
| RTI Elec | | UL 746 | 130 °C |
| RTI | | UL 746 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare