PA6 Quadrant EPP Nylatron® NSM
0
- Usages:Bearingsvalvesvalve componentswear stripsbushingscamsseals
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | g/cm³ | 1.14 -- | |
| Water absorption rate | % | 0.59 -- | |
| % | 6.3 -- | ||
| % | 2.0 -- | ||
| mg | 40.0 -- | ||
| mg | 76.01.1 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| MPa | 150 -- | ||
| Rockwell hardness | 81 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | HB -- | ||
| HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | MPa | 3150 1530 | |
| Tensile stress | Yield | MPa | 78.0 50.0 |
| MPa | 80.0 -- | ||
| Tensile strain | Yield | % | 5.0 -- |
| Break | % | 25 >50 | |
| compression stress | MPa | 31.0 -- | |
| MPa | 59.0 -- | ||
| MPa | 87.0 -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | kJ/m² | 3.5 -- | |
| Impact strength of simply supported beam without notch | kJ/m² | 75 -- |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 3.60 6.60 | |||
| 3.20 3.70 | |||
| Dissipation Factor | 0.012 0.14 | ||
| 0.016 0.050 | |||
| CTI | V | 600 600 | |
| Surface Resistivity | ohms | >1.0E+13 >1.0E+12 | |
| Volume resistivity | ohms·cm | >1.0E+14 >1.0E+12 | |
| dielectric strength | kV/mm | 25 17 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| cm/cm/°C | 8E-05 -- | ||
| cm/cm/°C | 9.5E-05 -- | ||
| thermal conductivity | W/m/K | 0.29 -- | |
| Service Temperature Minimum | °C | -30 -- | |
| maximum service temperature | °C | 90 -- | |
| °C | 105 -- | ||
| °C | 165 -- | ||
| °C | 75.0 -- | ||
| °C | 215 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.