'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
LDPE ATTANE™ 4203 STYRON US
33
- Properties:Low temperature resistancHigh impact resistanceCompliant with Canadian HExcellent elasticity andResistance to cracking an
- Usages:filmcontainerchipUsed for packaging
Compare
View PricesTechnical Data Sheet
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| turbidity | ASTM D1003 | 5 % | |
| gloss | 20 μm | ASTM D2457 | 48 |
| transparency | 20μm | ASTM D1746 | 93 |
| gloss | 45° | ASTM D2457 | 39 |
| turbidity | ASTM D1003 | 14 % |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Starting temperature of heat sealing | 陶氏企业测试 | 88 °C |
| Basic Performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 0.905 | |
| melt mass-flow rate | ASTM D1238 | 0.8 g/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Elongation at Break | 20μm (MD) | ASTM D882 | 445 % |
| tensile strength | 20 μm (MD) | ASTM D882 | 53 Mpa |
| Yield | ASTM D882 | 9 Mpa | |
| Puncture intensity | (20 μm) | 陶氏企业测试 | 22 J/cm |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vicat softening temperature | ASTM D1525 | 84 °C | |
| ASTM D1525 | 83.9 °C | ||
| Melting temperature | Internal Method | 123 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.80 g/10min |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | MD:Break | ASTM D882 | 32.4 Mpa |
| TD:Break | ASTM D882 | 30.0 Mpa | |
| elongation | MD:Break | ASTM D882 | 340 % |
| tensile strength | TD:Yield | ASTM D882 | 5.86 Mpa |
| MD:Yield | ASTM D882 | 6.21 Mpa | |
| Secant modulus | 2%Secant,TD | ASTM D882 | 93.8 Mpa |
| 1%Secant,TD | ASTM D882 | 113 Mpa | |
| 2%Secant,MD | ASTM D882 | 89.6 Mpa | |
| 1%Secant,MD | ASTM D882 | 98.6 Mpa | |
| Membrane strength | TD | ASTM D882 | 64.5 J/cm³ |
| MD | ASTM D882 | 45.5 J/cm³ | |
| Thin film puncture strength | Internal Method | 24.8 J/cm³ | |
| Internal Method | 48.9 N | ||
| Internal Method | 4.52 J | ||
| film thickness | 25 µm | ||
| elongation | TD:Break | ASTM D882 | 570 % |
| Dart impact | ASTM D1709B | >1100 g | |
| Elmendorf tear strength | MD | ASTM D1922 | 370 g |
| TD | ASTM D1922 | 520 g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.