| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Post curing time | | | 16 hr |
| STORAGE STABILITY | | | 6.0 min |
| stripping time | | | >60 min |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.19 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | Shore A | ASTM D2240 | 93to95 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Dynamic Properties | | | 3.14E+08 dynes/cm² |
| Dynamic Properties | | | 2.42E+08 dynes/cm² |
| Dynamic Properties | | | 0.0180 |
| Dynamic Properties | | | 0.0140 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compressive strength | | ASTM D695 | 2.48 MPa |
| compressive strength | | ASTM D695 | 4.83 MPa |
| compressive strength | | ASTM D695 | 6.89 MPa |
| compressive strength | | ASTM D695 | 9.31 MPa |
| compressive strength | | ASTM D695 | 12.1 MPa |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D412 | 9.65 MPa |
| tensile strength | | ASTM D412 | 13.8 MPa |
| tensile strength | | ASTM D412 | 48.3 MPa |
| elongation | Break | ASTM D412 | 650 % |
| tear strength | Split | ASTM D470 | 28 kN/m |
| compression set | | ASTM D395B | 35 % |
| compression set | | ASTM D395B | 50 % |
| Shore hardness | | ASTM D2632 | 57 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.