Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.20 % |
| Water absorption rate | | ISO 62 | 0.16 % |
| density | | ISO 1183 | 1.38 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.40 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 105 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2/1270 | 190 MPa |
| Tensile strain | Break | ISO 527-2/50 | 2.0 % |
| Flexural modulus | | ISO 178 | 16500 MPa |
| bending strength | | ISO 178 | 280 MPa |
| wear resistance | | ISO 8295 | 0.200 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | 9.0 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 65 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | <1.0E+5 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 290 °C |
| vicat | | ISO 306/B50 | 325 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.4E-04 cm/cm/°C |
| thermal conductivity | | ISO 8302 | 0.62 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.