Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 6.0 g/10min |
| density | | ISO 1183 | 0.890 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 54 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D523 | 90 |
| Haze ratio | | ASTM D1003 | 25 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 320 MPa |
| tensile strength | Yield | ISO 527-2 | 12.0 MPa |
| Nominal tensile fracture strain | | ISO 527-2 | >500 % |
| Flexural modulus | | ISO 178 | 280 MPa |
| bending strength | | ISO 178 | 12.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 15 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306 | 115 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.