PA6 LNP™ THERMOTUF™ PF006I SABIC INNOVATIVE US
115
- Properties:Thermal stabilityGlass fiber reinforcedAntistaticFiller: Glass fiber reinf30%Filler by weight
- Usages:Fitness equipmentPlastic bagElectronic and Electrical
CompareTechnical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 收缩率 | MD：24小时 | ASTMD955 | 0.10to0.30 % |
| TD：24hr | ASTMD955 | 0.90to2.0 % | |
| TD:24小时 | ISO294-4 | 0.62to0.67 % | |
| MD:24小时 | ISO294-4 | 0.11to0.30 % | |
| 吸水率 | 24hr,50%RH | ASTMD570 | 0.83 % |
| 平衡,23°C,50%RH | ISO62 | 0.83 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 热变形温度 | 0.45MPa,未退火,3.20mm | ASTMD648 | 139 °C |
| 热变形温度6 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 141 °C |
| 热变形温度 | 1.8MPa,未退火,3.20mm | ASTMD648 | 137 °C |
| 热变形温度6 | 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 135 °C |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| FlameRating | 1.5mm,TestingbySABIC | UL94 | HB |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 拉伸模量 | ASTMD638 | 16200 Mpa | |
| ISO527-2/1 | 9650 Mpa | ||
| 抗张强度 | 屈服 | ASTMD638 | 50.0 Mpa |
| 拉伸应力 | 屈服 | ISO527-2/5 | 35.0 Mpa |
| 抗张强度 | 断裂 | ASTMD638 | 97.4 Mpa |
| 拉伸应力 | 断裂 | ISO527-2/5 | 99.0 Mpa |
| 伸长率 | 断裂 | ASTMD638 | 8.2 % |
| 弯曲模量 | 50.0mm跨距 | ASTMD790 | 6830 Mpa |
| 弯曲强度5 | 断裂,50.0mm跨距 | ASTMD790 | 158 Mpa |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 悬壁梁缺口冲击强度5 | 23°C | ISO180/1A | 11 kJ/m² |
| 无缺口伊佐德冲击强度5 | 23°C | ISO180/1U | 54 kJ/m² |
| 装有测量仪表的落镖冲击 | 23°C,EnergyatPeakLoad | ASTMD3763 | 16.0 J |
| 多轴向仪器化冲击能量 | ISO6603-2 | 4.98 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.