PA6 BKV30F 000000 ENVALIOR WUXI

Form：Granules | Grade：Injection grade

Properties:

Heat aging

Typical Applications:

Automotive connectorsAutomotive componentsInstrument accessoriesElectronic and Electrical ApplicationsCommunication equipment

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive connectors \| Automotive components \| Instrument accessories \| Electronic and Electrical Applications \| Communication equipment
Properties:	Heat aging

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	55	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75mm	UL 94	V-0
Burning wire flammability index	1.5mm	IEC 60695-2-12	960	°C
Burning wire flammability index	Burning wire flammability index	0.8mm	IEC 60695-2-12	960	°C
UL flame retardant rating	1.6mm	UL 94	V-0
Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.8mm	IEC 60695-2-13	775	°C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	775	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	800	°C
Extreme Oxygen Index		ISO 4589-2	32	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	FlexuralStrainatFlexuralStrength5(23°C)		2.7	%
	bending strength	23°C	ISO 178	210	Mpa
	bending strength	bending strength	3.5%Strain	ISO 178/A	--	Mpa
Bending modulus	23°C	ISO 178/A	9800	Mpa
Tensile strain	Break,23°C	ISO 527-2/5	3.0	%
tensile strength	Break,23°C	ISO 527-2/5	150	Mpa
Tensile modulus	23°C	ISO 527-2/1	10800	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	8.1E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	2.2E-05	cm/cm/°C
Melting temperature		ISO 11357-3	224	°C
Vicat softening temperature		ISO 306/B120	210	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	204	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	218	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.5	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	5.0	%
Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO 294-4	0.080	%
	Shrinkage rate	MD:280°C,2.00mm2	ISO 294-4	0.22	%
		Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO 294-4	0.18	%
		Shrinkage rate	Shrinkage rate	TD:280°C,2.00mm2	ISO 294-4	0.62	%
Melt Volume Flow Rate (MVR)	260°C/2.16kg	ISO 1133	23.0	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength	23°C,1.00mm	IEC 60243-1	37	KV/mm
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ISO Shortcut		ISO 1874	PA6.GFHR.14-110.GF30;ISO1043-PAGFFR(30+40+72)

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.