Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTMD570 | 0.060 % |
| density | | ASTMD792 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 9.0 g/10min |
| Shrinkage rate | | ASTMD955 | 0.20到0.50 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 106 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Limiting Oxygen Index | | ASTMD2863 | 26 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 120 J/m |
| Suspended wall beam without notch impact strength | | ASTMD256 | 650 J/m |
| Dart impact equipped with measuring instruments | | ASTMD3763 | 22.6 J |
| Impact strength of cantilever beam gap | | ASTMD256 | 96 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 6200 MPa |
| tensile strength | Break | ASTMD638 | 90.3 MPa |
| elongation | Break | ASTMD638 | 2.6 % |
| Flexural modulus | | ASTMD790 | 5800 MPa |
| bending strength | | ASTMD790 | 160 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| High arc combustion index (HAI) | | UL746 | PLC 4 |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | PLC 4 |
| Hot wire ignition (HWI) | | UL746 | PLC 4 |
| dielectric strength | | ASTMD149 | 17 kV/mm |
| dielectric constant | | ASTMD150 | 2.86 |
| dielectric constant | | ASTMD150 | 2.86 |
| Dissipation Factor | | ASTMD150 | 8E-04 |
| Dissipation Factor | | ASTMD150 | 8E-04 |
| arc resistance | | ASTMD495 | PLC7 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Elec | | UL746 | 90.0 °C |
| RTI Imp | | UL746 | 90.0 °C |
| RTI | | UL746 | 90.0 °C |
| | ASTMD648 | 141 °C |
| | ASTMD648 | 143 °C |
| | ASTMD648 | 135 °C |
| | ASTMD648 | 138 °C |
| | ASTME831 | 2.9E-05 cm/cm/°C |
| | ASTME831 | 8.3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.