PPO StarAir® LXS115
9
- Properties:Flame retardant
- Usages:Electronic and Electrical Applications
CompareTechnical Data Sheet
| processability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dry conditions | 120-2h | ||
| screw speed | 60cm3\s rpm | ||
| Temperature | 60-80 °C | ||
| Melt Temperature | 260 °C | ||
| pressure | 15kg Mpa | ||
| 100kg\cm2 Mpa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation at break | ASTM D638/ISO 527 | 28 % | |
| Tensile modulus | ASTM D638/ISO 527 | 2250 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 75 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 119 | |
| Flexural modulus | ASTM D790/ISO 178 | 95 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 95 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | ASTM D150/IEC 60250 | 100 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.10 | |
| Mold Shrinkage | ASTM D955 | 0.5-0.7 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 20 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.10 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTM D648/ISO 75 | 150 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.