| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 1.0 % |
| Shrinkage rate | | 内部方法 | 0.30 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| water content | | ISO 15512 | <0.080 % |
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 加纤30% 增强级 冲击改性 |
| purpose | | | 车辆配件 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 725 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 11000 Mpa |
| tensile strength | | ISO 527-2 | 130 Mpa |
| Tensile strain | | ISO 527-2 | 2.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ISO 180/1U | 60 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 65 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 205 °C |
| vicat | | ISO 306/B | 210 °C |
| melting temperature | | ISO 11357-3 | 225 °C |
| Heat distortion temperature | | ISO 75-2/B | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.