PA66 A1S25 G50
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183/A | 1.59 g/cm³ | |
| ISO 1183/A | 1.59 g/cm³ | ||
| Humidity | ISO 15512/B | <0.25 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 95 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179/1eA | 16 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eU | 95 kJ/m² | |
| Tensile modulus | ISO 527-2 | 15500 MPa | |
| tensile strength | Break | ISO 527-2 | 230 MPa |
| Tensile strain | Break | ISO 527-2 | 2.5 % |
| Flexural modulus | ISO 178 | 13500 MPa | |
| bending strength | ISO 178 | 360 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 16 kJ/m² | |
| Tensile modulus | ISO 527-2 | 15500 MPa | |
| tensile strength | Break | ISO 527-2 | 230 MPa |
| Tensile strain | Break | ISO 527-2 | 2.5 % |
| Flexural modulus | ISO 178 | 13500 MPa | |
| bending strength | ISO 178 | 360 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ISO 75-2/A | 250 °C | |
| vicat | ISO 306/B | >230 °C | |
| Hot deformation temperature (HDT) | ISO 75-2/A | 250 °C | |
| vicat | ISO 306/B | > 230 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.