Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.45 g/cm³ |
| Water absorption rate | | | <0.10 % |
| Shrinkage rate | | DIN 16901 | 0.20to0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 35 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 15000 MPa |
| tensile strength | Break | ISO 527-2 | 170 MPa |
| Tensile strain | Yield | ISO 527-2 | 2.0 % |
| Flexural modulus | | ISO 178 | 13000 MPa |
| bending strength | | ISO 178 | 240 MPa |
| Bending Strain | | ISO 178 | 2.5 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | <1.0E+6 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 260 °C |
| Linear coefficient of thermal expansion | | DIN 53752 | 3E-05 cm/cm/°C |
| thermal conductivity | | DIN 52612 | 0.45 W/m/K |
| Continuous use temperature | | UL 746B | 250 °C |
| maximum service temperature | | | 280 °C |
| vicat | | ISO 306/A | 320 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.