PC+Polyester XYLEX™ X8303CL resin
0
- Usages:label
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO62 | 0.50 % | |
| ISO62 | 0.20 % | ||
| density | ASTMD792,ISO1183 | 1.20 g/cm³ | |
| melt mass-flow rate | ASTMD1238 | 30 g/10min | |
| Melt volume flow rate | ISO1133 | 27.5 cm³/10min | |
| Shrinkage rate | 内部方法 | 0.40到0.80 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| fracture | ASTMD638 | 44.0 MPa | |
| ISO527-2/50 | 43.0 MPa | ||
| yield | ASTMD638 | 5.0 % | |
| ISO527-2/50 | 6.0 % | ||
| fracture | ASTMD638 | 140 % | |
| ISO527-2/50 | 140 % | ||
| yield | ASTMD790 | 72.0 MPa | |
| ASTMD638 | 46.0 MPa | ||
| ISO527-2/50 | 48.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179/1eA | 14 kJ/m² | |
| Dart impact equipped with measuring instruments | ASTMD3763 | 65.0 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Horizontally:- | ASTME831 | 9E-05 cm/cm/°C | |
| Horizontally: | ISO11359-2 | 9.8E-05 cm/cm/°C | |
| Flow:- | ASTME831 | 9E-05 cm/cm/°C | |
| Flow: | ISO11359-2 | 9.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.