PC IR2210 SABIC INNOVATIVE SPAIN

Form：Granules

Properties:

Thermal stabilityHigh mobility

Typical Applications:

Automotive componentsCasters

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive components \| Casters
Properties:	Thermal stability \| High mobility

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ASTM D542，ISO 489	1.586
Transmittance rate	2540 μm	ASTM D1003	88.0 to 90.0	%
turbidity	2540 μm	ASTM D1003	< 0.80	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23℃	ASTM D4812	无断裂	J/m
	Suspended wall beam without notch impact strength	23℃，80103	ISO 180/1U	无断裂	kJ/m²
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30℃，80103	ISO 180/1U	无断裂	kJ/m²
Dart impact	23℃	ASTM D3763	65	J
Impact strength of cantilever beam gap	23℃，80103	ISO 180-1A	70	kJ/m²
	Impact strength of cantilever beam gap	-30℃，80103	ISO 180-1A	12	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃	ASTM D256	800	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield，2 mm/min	ISO 178	90	Mpa
bending strength	bending strength	Yield，1.3 mm/min，50 mmSpan	ASTM D790	90	Mpa
Bending modulus	2 mm/min	ISO 178	2300	Mpa
Bending modulus	Bending modulus	1.3 mm/min，50 mmSpan	ASTM D790	2300	Mpa
Tensile strain	Break，50 mm/min	ISO 527	> 70	%
	Tensile strain	Break，I型，50 mm/min	ASTM D638	> 70	%
		Tensile strain	Yield，50 mm/min	ISO 527	6	%
		Tensile strain	Tensile strain	Yield，I型，50 mm/min	ASTM D638	6	%
tensile strength	Yield，50 mm/min	ISO 527	63	Mpa
tensile strength	tensile strength	Yield，I型，50 mm/min	ASTM D638	63	Mpa
Tensile modulus	1 mm/min	ISO 527	2350	Mpa
Tensile modulus	Tensile modulus	50 mm/min	ASTM D638	2350	Mpa
Rockwell hardness	R-Scale	ISO 2039-2	120
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	120
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa， 80104，64 mmSpan	ISO 75-2/Af	127	°C
Vicat softening temperature	B50	ISO 306	143	°C
Vicat softening temperature	Vicat softening temperature	B50	ASTM D1525	143	°C
Hot deformation temperature	0.45 MPa，3.2 mm	ASTM D648	138	°C
	Hot deformation temperature	0.45 MPa， 80104，64 mmSpan	ISO 75-2/Bf	138	°C
	Hot deformation temperature	Hot deformation temperature	1.8 MPa，3.2 mm	ASTM D648	127	°C
Ball indentation test	125℃+/- 2℃	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD，-40℃~95℃	ASTM E831	0.000070	1/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD，23℃~80℃	ISO 11359-2	0.000070	1/℃
thermal conductivity		ASTM C177	0.2	W/m/℃
thermal conductivity	thermal conductivity		ISO 8302	0.2	W/m/℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium，23℃	ASTM D570	0.35	%
Water absorption rate	Water absorption rate	Saturation，23℃	ISO 62	0.35	%
Shrinkage rate	MD：3.2 mm	Internal Method	0.50 - 0.70	%
Shrinkage rate	Shrinkage rate	MD	Internal Method	0.50 - 0.70	%
Melt Volume Flow Rate (MVR)	300℃，1.2 kg	ISO 1133	9	cm3/10min
melt mass-flow rate	300℃，1.20kg	ASTM D1238	10	g/10min
density		ASTM D792	1.2	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	60 Hz	ASTM D150	3
Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3
Dissipation factor	60 Hz	ASTM D150	0.001
Dissipation factor	Dissipation factor	1 MHz	ASTM D150	0.01
Volume resistivity		ASTM D257，IEC 60093	> 1.0E+15	ohms·cm
Dielectric strength	1.6 mm	ASTM D149，IEC 60243-1	27	KV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.