| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.35 g/cm³ |
| Shrinkage rate | | ASTM D995 | 1.30 % |
| Shrinkage rate | | ASTM D995 | 1.50 % |
| Water absorption rate | | ASTM D570 | 0.02 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 100 M（Scale） |
| Rockwell hardness | | ASTM D785 | 121 R |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| coefficient of friction | | ASTM D3702 | 0.35 |
| tensile strength | | ASTM D638 | 80 MPa |
| elongation at break | | ASTM D638 | >15 % |
| Tensile modulus | | ASTM D638 | 4200 MPa |
| Tensile modulus | | ASTME132 | 0.38 |
| bending strength | | ASTM D790 | 130 MPa |
| Flexural modulus | | ASTM D790 | 3800 MPa |
| Impact strength of cantilever beam gap | | ASTM D256 | 40 J/m |
| coefficient of friction | | ASTM D3702 | 0.40 |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL -94 | V-0 0.75mm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+16 Ω.cm |
| dielectric strength | | ASTM D149 | 23 KV/mm |
| dielectric constant | | ASTM D150 | 3.3 1MHz |
| Dissipation Factor | | ASTM D150 | 2E-03 1MHz |
| Dissipation Factor | | ASTM D495 | 125 s |
| Dissipation Factor | | ASTM D3638 | 135 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 200 °C |
| Heat distortion temperature | | ASTM D648 | 110 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 4E-05 cm/cm／°C |
| Linear coefficient of thermal expansion | | ASTM D696 | 4E-05 cm/cm／°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.