PVC

PVC polyvic® M-1838-GL 06 Unipack Plasindo

Compare

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity		ASTM D1003	89.6 %
transmissivity	transmissivity		ASTM D1003	89.6 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256	72 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256	72 J/m

flammability	Test Condition	Test Method	Test Result
Burning rate		ASTM D635	4.4 mm/min
Burning rate	Burning rate		ASTM D635	4.4 mm/min

mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ASTM D638	50.0 MPa
elongation	Break	ASTM D638	17 %
tensile strength		ASTM D638	50.0 MPa
elongation	Break	ASTM D638	17 %

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ASTM D256	79.0 °C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	68.0 °C
Vicat softening temperature		ASTM D256	79.0 °C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	68.0 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.33 g/cm³
density	density		ASTM D792	1.33 g/cm³

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreA	ASTM D2240	92
Shore hardness	Shore hardness	ShoreA	ASTM D2240	92
Rockwell hardness	R-Scale	ASTM D785	110
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	110

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.