LDPE HP4024W SABIC SAUDI

Form：Granules | Grade：Injection grade

Properties:

low densityLow friction coefficientSmoothnessoptical performance Anti caking propertyFood contact compliance

Typical Applications:

Laundry bagfilmchip

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Laundry bag \| film \| chip
Properties:	low density \| Low friction coefficient \| Smoothness \| optical performance \| Anti caking property \| Food contact compliance

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
turbidity	50.0μm,Blown Film	ASTM D1003	<9.0	%
gloss	60°,50.0μm,Blown Film	ASTM D2457	>100
gloss	gloss	20°,50.0μm,Blown Film	ASTM D2457	>50
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Friction coefficient		ISO 8295	<20	%
tensile strength	Yield,0.0500mm	ISO 527-2	11.0	Mpa
Tensile modulus	0.0500mm	ISO 527-2	260	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 3146	111	°C
Vicat softening temperature		ISO 306/A50	92.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190°C/2.16kg	ISO 1133	4.0	g/10min
density	23°C	ISO 1183	0.923	g/cm³
film	Test Condition	Test Method	Test Result	Test Unit
tensile strength	TD:Break,50μm,Blown Film	ISO 527-3	16.0	Mpa
tensile strength	tensile strength	MD:Break,50μm,Blown Film	ISO 527-3	19.0	Mpa
film thickness			15-40micron
film thickness	film thickness			50	µm
Dart impact	50μm,Blown Film	ASTM D1709	100	g
elongation	TD:Break,50μm,Blown Film	ISO 527-3	600	%
elongation	elongation	MD:Break,50μm,Blown Film	ISO 527-3	300	%
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Inflation ratio (BUR)			2.00to3.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.