Technical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| colour | | | Amber |
| colour | | | Grey |
| density | | | 1.22 g/cm³ |
| density | | | 2.68 g/cm³ |
| density | | | 23到34 Pa·s |
| density | | | 1.0 hr |
| density | Pot Life | | 480 min |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| | | 按重量计算的混合比:100 |
| | | 按重量计算的混合比:15 |
| | | 52 wk |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Particle size | | | <50.0 µm |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Supporting hardness | | | 89 |
| LapShearStrength | | | 8.38 MPa |
| | | 5.40 |
| Volume resistivity | | | >2.0E+13 ohms·cm |
| Dissipation Factor | | | 4E-03 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| WeightLossonHeating | | | 0.080 % |
| WeightLossonHeating | | | 0.22 % |
| Operating | | | 5.40 GPa |
| Operating | | | 3.00 |
| WeightLossonHeating | | | <0.050 % |
| DegradationTemperature | | TGA | 413 °C |
| Shear Strength | | | 11.7 MPa |
| Operating | | | -55到260 °C |
| Operating | | | -55到360 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | >80.0 °C |
| | | 3.4E-05 cm/cm/°C |
| | | 1.3E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 1.1 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare