Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO 1133 | 34.0 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 0.80 % |
| Water absorption rate | | ISO 62 | 1.1 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 102 Mpa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 2200 Mpa |
| tensile strength | | ISO 527-2 | 50.0 Mpa |
| Tensile strain | | ISO 527-2 | 3.2 % |
| Flexural modulus | | ISO 178 | 2200 Mpa |
| bending strength | | ISO 178 | 74.0 Mpa |
| film | Test Condition | Test Method | Test Result |
|---|
| elongation | | | 20 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| relative permittivity | | IEC 60250 | 2.90 |
| Dissipation Factor | | IEC 60250 | 0.015 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| 0.45MPa, annealing | | ISO 75-2/B | 88.0 °C |
| 1.8MPa, annealing | | ISO 75-2/A | 66.0 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare