Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.35到1.45 g/cm³ |
| Shrinkage rate | | ASTMD955 | 1.0 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTMD2457 | 80到85 |
| transmissivity | | ASTMD1003 | 89.0到93.0 % |
| Haze ratio | | ASTMD1003 | 15到20 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| WaterActivity | | 内部方法 | 0.500到0.650 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Itself - Dynamic | ASTMD1894 | 0.17 |
| Itself - Static | ASTMD1894 | 0.22 |
| film | Test Condition | Test Method | Test Result |
|---|
| Water vapor permeability | | ASTME96 | 35到40 g/m²/24hr |
| Film thickness - tested | | | 250 µm |
| Secant modulus MD | | ASTMD882 | 2200到2400 MPa |
| tensile strength | | ASTMD882 | 42.0到46.0 MPa |
| elongation | | ASTMD882 | 20到36 % |
| Elmondov tear strength MD | | ASTMD1922 | 3500到5500 g |
| oxygen permeability | | ASTMD1434 | 0.130 cm³/m²/24hr |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | ASTME1356 | 40.0到45.0 °C |
| vicat | | ASTMD1525 | 130到135 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.