PEI ProPolymers PEI 1000
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.60to0.90 % | |
| Water absorption rate | ASTM D570 | 0.25 % | |
| density | ASTM D792 | 1.27 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 9.0 g/10min | |
| Shrinkage rate | ASTM D955 | 0.50to0.80 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M-Scale | 109 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ASTM D638 | 110 MPa |
| elongation | Yield | ASTM D638 | 60 % |
| Break | ASTM D638 | 6.5 % | |
| Flexural modulus | ASTM D790 | 3590 MPa | |
| bending strength | ASTM D790 | 162 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 53 J/m | |
| ASTM D256 | 6.00 kJ/m² | ||
| Suspended wall beam without notch impact strength | ASTM D256 | 1300 J/m | |
| ASTM D256 | 140 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ASTM D648 | 210 °C | |
| ASTM D648 | 202 °C | ||
| vicat | ASTM D1525 | 219 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.