| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.38 g/cm³ |
| spiral flow length | | 内部方法 | 10.0 CM |
| Shrinkage rate | | ISO 294-4 | 0.90 % |
| Shrinkage rate | | ISO 294-4 | 0.50 % |
| Water absorption rate | | ISO 62 | 0.060 % |
| Water absorption rate | | ISO 62 | 0.40 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 86 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | ISO 11443 | 450 Pa·s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 7500 Mpa |
| tensile strength | | ISO 527-2 | 140 Mpa |
| tensile strength | | ISO 527-2 | 80.0 Mpa |
| tensile strength | | ISO 527-2 | 45.0 Mpa |
| tensile strength | | ISO 527-2 | 25.0 Mpa |
| Tensile strain | | ISO 527-2 | 4.0 % |
| Flexural modulus | | ISO 178 | 7000 Mpa |
| bending strength | | ISO 178 | 240 Mpa |
| compression stress | | ISO 604 | 200 Mpa |
| compression stress | | ISO 604 | 130 Mpa |
| compression stress | | ISO 604 | 40.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 5.5 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1U | 60 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/A | 6.0 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 55 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| dielectric strength | | IEC 60243-1 | 24 KV/mm |
| dielectric constant | | IEC 60250 | 3.10 |
| Dissipation Factor | | IEC 60250 | 5E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 4 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ISO 11359-2 | 3E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| specific heat | | DSC | 1700 J/kg/°C |
| thermal conductivity | | ISO 22007-4 | 0.30 W/m/K |
| Heat distortion temperature | | ISO 75-2/Af | 298 °C |
| Glass Transition Temperature | | ISO 11357-2 | 143 °C |
| melting temperature | | ISO 11357-3 | 343 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 2.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.