Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.40 % |
| Water absorption rate | | ISO 62 | >0.020 % |
| density | | ISO 1183 | 1.76 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 101 M（Scale） |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 172 MPa |
| elongation at break | | ISO 527-2 | 2 % |
| bending strength | | ISO 178 | 262 MPa |
| Flexural modulus | | ISO 178 | 16300 MPa |
| Charpy Notched Impact Strength | | ISO 179/1eA | 9 kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL -94 | V-0 0.80mm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 14 KV/mm |
| dielectric constant | | IEC 60250 | 4.90 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/Af | 269 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 2.2E-05 cm/cm／°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 2.6E-05 cm/cm／°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.