Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 1.1 % |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| Water absorption rate | | ISO 62 | 6.9 % |
| Water absorption rate | | ISO 62 | 2.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO 3795 | 24 mm/min |
| UL flame retardant rating | | UL 94, IEC 60695-11-10, -20 | HB |
| UL flame retardant rating | | UL 94, IEC 60695-11-10, -20 | HB |
| Limiting Oxygen Index | | ISO 4589-2 | 24 % |
| FMVSS flammability | | FMVSS 302 | SE/B |
| atomization | | ISO 6452 | 95 % |
| atomization | | ISO 6452 | 3.0E-4 g |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 9800 Mpa |
| Tensile stress | | ISO 527-2 | 195 Mpa |
| Tensile strain | | ISO 527-2 | 3.5 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 60 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 80 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| Melt density | | | 1.21 g/cm³ |
| Specific Heat Capacity of Melt | | | 2290 J/kg/°C |
| Thermal Conductivity of Melt | | | 0.21 W/m/K |
| Emission of Organic Compounds | | VDA 277 | 6.00 µgC/g |
| Odor | | VDA 270 | 4.50 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 62631-3-2 | -- ohms |
| Volume resistivity | | IEC 62631-3-1 | 1.0E+11 ohms·m |
| Dissipation Factor | | IEC 62631-2-1 | 0.016 |
| Dissipation Factor | | IEC 62631-2-1 | 0.016 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 0 |
| CTI | | IEC 60112 | 600 V |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| Drying time - hot air dryer | | | 2.0 到 4.0 hr |
| Suggested maximum moisture content | | | 0.20 % |
| Processing (melt) temperature | | | 285 到 305 °C |
| Melt Temperature, Optimum | | | 295 °C |
| Temperature | | | 70 到 120 °C |
| Mold Temperature, Optimum | | | 100 °C |
| pressure holding | | | 50.0 到 100 Mpa |
| pressure holding | | | yes |
| Hold Pressure Time | | | 3.00 s/mm |
| Maximum Screw Tangential Speed | | | 12 m/min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75-2/B | 260 °C |
| | ISO 75-2/A | 253 °C |
| Glass transition temperature 3 | | ISO 11357-2 | 80.0 °C |
| Melting temperature 3 | | ISO 11357-3 | 262 °C |
| | ISO 11359-2 | 2.8E-5 cm/cm/°C |
| | ISO 11359-2 | 9.5E-5 cm/cm/°C |
| Effective Thermal Diffusivity | | | 6.85E-8 m²/s |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.