Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.04 g/cm³ |
| thickness | | | 177.8to330.2 µm |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2280 MPa |
| tensile strength | | ASTM D638 | 36.5 MPa |
| elongation | | ASTM D638 | 3.0 % |
| Flexural modulus | | ASTM D790 | 2210 MPa |
| bending strength | | ASTM D790 | 52.4 MPa |
| Bending layering | | ASTM D790 | 31.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256A | 110 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 0.10to0.32 kV/mm |
| dielectric strength | | IEC 60112 | 28 kV/mm |
| dielectric constant | | ASTM D150 | 2.60to2.90 |
| Dissipation Factor | | ASTM D150 | 4.6E-3到5.3E-3 |
| Volume resistivity | | ASTM D257 | 6.0E+13到3.0E+14 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 95.6 °C |
| Heat distortion temperature | | ASTM D648 | 82.2 °C |
| Glass Transition Temperature | | DMA | 108 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 8.8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.