PP TechnoFiber PP LGF 50-10-01 HI
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.31 g/cm³ | |
| Shrinkage rate | ISO294-4 | 0.20 % | |
| density | ISO1183 | 1.31 g/cm³ | |
| Shrinkage rate | ISO294-4 | 0.20 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ISO178 | 11200 MPa | |
| Bending stress | ISO178 | 140 MPa | |
| Tensile modulus | ISO527-2/1 | 11200 MPa | |
| Tensile stress | Yield | ISO527-2/50 | 125 MPa |
| Tensile strain | Yield | ISO527-2/50 | 2.1 % |
| Flexural modulus | ISO178 | 11200 MPa | |
| Bending stress | ISO178 | 140 MPa | |
| Tensile modulus | ISO527-2/1 | 11200 MPa | |
| Tensile stress | Yield | ISO527-2/50 | 125 MPa |
| Tensile strain | Yield | ISO527-2/50 | 2.1 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179/1eA | 22 kJ/m² | |
| ISO179/1eA | 22 kJ/m² | ||
| ISO179/1eA | 23 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO179/1eU | 60 kJ/m² | |
| ISO179/1eU | 60 kJ/m² | ||
| Charpy Notched Impact Strength | ISO179/1eA | 23 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO179/1eU | 60 kJ/m² | |
| ISO179/1eU | 60 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO11357-3 | 165 °C | |
| ISO11359-2 | 1.3E-05 cm/cm/°C | ||
| ISO11359-2 | 1.7E-05 cm/cm/°C | ||
| ISO75-2/B | 160 °C | ||
| ISO75-2/A | 151 °C | ||
| ISO75-2/C | 130 °C | ||
| ISO75-2/B | 160 °C | ||
| ISO75-2/A | 151 °C | ||
| ISO75-2/C | 130 °C | ||
| melting temperature | ISO11357-3 | 165 °C | |
| ISO11359-2 | 1.3E-05 cm/cm/°C | ||
| ISO11359-2 | 1.7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.