PC+AS(SAN)

PC+AS(SAN) T88 GF-20 Covestro - Polycarbonates

Properties:
Filler glass fiber reinforced material 20% filler by weight
Compare

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	23°C	ISO 527-2	120 MPa
Elongation at Break	23°C	ISO 527-2	2.40 %
Tensile modulus	23°C	ISO 527-2	7200 MPa
Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.00 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	8.00 kJ/m²

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	129 °C
Hot deformation temperature	Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	119 °C
Vicat softening temperature		ISO 306/B50	128 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	3E-05 cm/cm／°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	6.5E-05 cm/cm／°C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.29 g/cm³
Shrinkage rate	MD2.0mm	ISO 294-4	0.40 %
Shrinkage rate	Shrinkage rate	TD2.0mm	ISO 294-4	0.30 %
Water absorption rate	(23°C,24hr)	ISO 62	0.40 %
Water absorption rate	Water absorption rate	(23°C,50RH)	ISO 62	0.20 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength		IEC 60243-1	35 KV/mm
Dielectric constant	23°C	IEC 60250	3.20 1MHz
Dissipation factor	23°C	IEC 60250	8.5E-03 1MHz
Volume resistivity		IEC 60093	1E+16 Ω.cm
Surface resistivity		IEC 60093	1E+17 Ω.cm
Dissipation factor	相对漏电起痕指数	IEC 60112	150 V

flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	HB 0.85mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.