Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.25 -- |
| Shrinkage rate | | % | 0.40到0.60 -- |
| Water absorption rate | | % | 1.0 -- |
| HeatStability | | °C | 115到120 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 122 110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | % | 4.0 6.0 |
| Flexural modulus | | MPa | 6000 3500 |
| bending strength | | MPa | 175 110 |
| Tensile modulus | | MPa | 7000 5000 |
| tensile strength | | MPa | 140 95.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| | kJ/m² | 9.0 14 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 -- |
| dielectric strength | | kV/mm | 22 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | >200 -- |
| | °C | >240 -- |
| melting temperature | | °C | 250到260 -- |
| | cm/cm/°C | 3E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.