GPPS S334
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D-792 | 1.04 g/cm | |
| Shrinkage rate | ASTM D-955 | 0.40-0.70 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D-1238 | 4.0 g/10min | |
| Water absorption rate | ASTM D-570 | 0.040 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D-256 | 98.1 J/m | |
| Rockwell hardness | ASTM D-785 | 80 L scale | |
| tensile strength | ASTM D-638 | 37.3 MPa | |
| elongation at break | ASTM D-638 | 30 % | |
| Flexural modulus | ASTM D-790 | 2160 MPa | |
| bending strength | ASTM D-790 | 53.9 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D-257 | 1E+17 ohm.cm | |
| dielectric constant | ASTM D-150 | 2.500 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D-648 | 98.0 ℃ | |
| vicat | ASTM D-1525 | 98.0 ℃ | |
| ASTM D-1525 | 91.0 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.