Technical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| | | 6.0到10 min |
| | | 0.10 Pa·s |
| | | 0.70 Pa·s |
| | | 1.5 Pa·s |
| | | 26 hr |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.22 g/cm³ |
| density | | | 1.23 g/cm³ |
| density | Base Resin | | 1.35 g/cm³ |
| Shrinkage rate | | ASTMD2566 | 0.10到0.50 % |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Supporting hardness | | ASTMD2240 | 80到90 |
| tensile strength | | ASTMD638 | 60.7 MPa |
| elongation | Break | ASTMD638 | 5.0 % |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Resin | | 按重量计算的混合比:100按容量计算的混合比:90 |
| Hardener | | 按重量计算的混合比:100按容量计算的混合比:100 |
| Demold Time | | 60到180 min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTMD790 | 80.7 MPa |
| Flexural modulus | | ASTMD790 | 2070 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 53 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 75.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.