PC Makrolon® FR6005 013756
148
- Properties:Easy to demouldImpact resistanceAging resistance
- Usages:Electronic and electrical enclosure
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1200 kg/m3 | |
| Shrinkage rate | ISO 2577 | 0.6-0.8 % | |
| ISO 2577 | 0.6-0.8 % | ||
| melt mass-flow rate | ISO 1133 | 9 cm3/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527 | 2300 Mpa | |
| tensile strength | ISO 527 | 62 Mpa | |
| ISO 527 | 66 Mpa | ||
| elongation | ISO 527 | 6 % | |
| elongation at break | ISO 527 | 50 % | |
| ISO 527 | 135 % | ||
| bending strength | ISO 178 | 90 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| Impact strength of cantilever beam gap | ISO 180 | 60 kJ/m² | |
| ISO 180 | 50 kJ/m² | ||
| ISO 180 | 15 kJ/m² | ||
| ISO 179 | 68 kJ/m² | ||
| ISO 179 | 50 kJ/m² | ||
| ISO 179 | 20 kJ/m² | ||
| Maximum puncture resistance at 23 ° C | ISO 6603 | 5100 N | |
| Maximum puncture resistance -30 ° C | ISO 6603 | 6100 N | |
| Puncture Resistance | ISO 6603 | 54 J | |
| ISO 6603 | 55 J |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-2 | |
| UL 94 | V-0 | ||
| UL 94 | V-0 | ||
| UL 94 | V-1 | ||
| UL 94 | V-0 | ||
| UL 94 | V-0 | ||
| Glow wire ignition temperature (GWIT) | ISO 11359-2 | 875 °C | |
| ISO 11359-2 | 850 °C | ||
| ISO 11359-2 | 900 °C | ||
| Relative temperature of heating wire | ISO 11359-2 | 850 °C | |
| ISO 11359-2 | 960 °C | ||
| ISO 11359-2 | 960 °C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 90000000000000000 Ω.m | |
| Surface Resistivity | IEC 60093 | 400000000000000000 Ω | |
| CTI solution A | IEC 60112 | 200 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75 | 121 °C | |
| ISO 75 | 136 °C | ||
| vicat | ISO 306 | 142 °C | |
| ISO 306 | 144 °C | ||
| Linear coefficient of thermal expansion | ISO 11359 | 0.000070 cm/cm/°C | |
| ISO 11359 | 0.000070 cm/cm/°C | ||
| Ball indentation test | ISO 11359-2 | 134 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.