Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| | | 按容量计算的混合比:4.2按重量计算的混合比:7.2 |
| | | 按容量计算的混合比:1.0按重量计算的混合比:1.0 |
| | | 52 wk |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Color | | | Black |
| Color | | | Colorless |
| density | | | 0.938 g/cm³ |
| density | | | 1.62 g/cm³ |
| | ASTM D2393 | 0.010 Pa·s |
| | ASTM D2393 | 5.0 Pa·s |
| | ASTM D2393 | 120 Pa·s |
| Curing Time | | | 18 hr |
| Curing Time | | | 36 hr |
| Curing Time | | | 480to600 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Hardness (Shore) | | ASTM D2240 | 85 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 16 kV/mm |
| dielectric constant | | ASTM D150 | 3.00 |
| Dissipation Factor | | ASTM D150 | 0.010 |
| Volume resistivity | | ASTM D257 | 6E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | 72.0to78.0 °C |
| | | 3.2E-05 cm/cm/°C |
| thermal conductivity | | | 0.65 W/m/K |
| Usage temperature | | | 105 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.