Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ISO 1183 | 1.30 g/cm³ |
Shrinkage rate | | | 1.2 % |
Water absorption rate | | ISO 62 | 0.50 % |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | M-Scale | ASTM D785 | 99 |
Filling analysis | Test Condition | Test Method | Test Result |
---|
MeltViscosity | | 内部方法 | 0.440 kPa |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
shear modulus | | ISO 15310 | 1150 MPa |
shear strength | | ASTM D732 | 90.0 MPa |
Poisson's ratio | | ASTM D638 | 0.36 |
tensile strength | Yield | ISO 527-2 | 100 MPa |
tensile strength | | ISO 527-2 | 115 MPa |
Tensile strain | Break | ISO 527-2 | 40 % |
Tensile strain | | ISO 527-2 | 20 % |
Flexural modulus | | ISO 178 | 4100 MPa |
Flexural modulus | | ISO 178 | 4000 MPa |
bending strength | | ISO 178 | 165 MPa |
bending strength | | ISO 178 | 170 MPa |
compression stress | | ISO 604 | 135 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ISO 180 | 7.5 kJ/m² |
Impact strength of cantilever beam gap | | ISO 180 | 4.7 kJ/m² |
Suspended wall beam without notch impact strength | | ISO 180 | 无断裂 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Linear coefficient of thermal expansion | | ASTM D696 | 4.7E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ASTM D696 | 1.1E-04 cm/cm/°C |
RTI Elec | | UL 746 | 260 °C |
RTI Imp | | UL 746 | 260 °C |
RTI | | UL 746 | 260 °C |
melting temperature | | | 340 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.