Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.17 g/cm³ |
| Shrinkage rate | | | 0.60 - 1.0 % |
| Water absorption rate | | ASTM D570 | 1 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 78 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 115 |
| tensile strength | | ASTM D638 | 54.9 Mpa |
| Tensile strain | | ASTM D638 | 30 % |
| Flexural modulus | | ASTM D790 | 2750 Mpa |
| bending strength | | ASTM D790 | 83.4 Mpa |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 100000000000000 ohms·cm |
| dielectric strength | | ASTM D149 | 24 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 235 °C |
| Heat distortion temperature | | ASTM D648 | 95 °C |
| melting temperature | | DSC | 260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare