Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 0.908 g/cm³ |
| melt mass-flow rate | | 内部方法 | 1.3 g/10min |
| Water absorption rate | | IEC 60811 | 1.00 mg/cm² |
| hardness | Test Condition | Test Method | Test Result |
|---|
| IRHD hardness | | ISO 48 | 91 |
| Shore hardness | | ISO 868 | 32 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | IEC 60811 | 7.00 MPa |
| tensile strength | Break | IEC 60811 | 20.5 MPa |
| elongation | Break | IEC 60811 | 470 % |
| aging | Test Condition | Test Method | Test Result |
|---|
| Changes in mechanical properties after hot air aging test | | IEC 60811 | 10 % |
| Changes in mechanical properties after hot air aging test | | IEC 60811 | 5 % |
| Bending test variation - in air, | | IEC 60811 | 无开裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | IEC 60502 | 5000 Mohms·km |
| dielectric constant | | IEC 60502 | 15000 Mohms·km |
| Dissipation Factor | | ASTM D150 | 8E-04 |
| dielectric constant | | ASTM D150 | 2.30 |
| dielectric strength | | ASTM D149 | 39 kV/mm |
| Volume resistivity | | IEC 60502 | 1.3E+15 ohms·cm |
| Volume resistivity | | IEC 60502 | 4.1E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermosetting | | IEC 60811 | 0.0 % |
| thermosetting | | IEC 60811 | 30 % |
| thermosetting | | IEC 60811 | 50 % |
| thermosetting | | IEC 60811 | 0.0 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare