Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.80 % |
| density | | ASTM D792 | 1.21 g/cm³ |
| density | | ISO 1183 | 1.21 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.80 % |
| Shrinkage rate | | ISO 2577 | 0.80 % |
| Shrinkage rate | | ISO 2577 | 0.80 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 70 |
| Shore hardness | | ISO 868 | 70 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressiveLoad | | ASTM D575 | 31.7 MPa |
| CompressiveLoad | | ASTM D575 | 41.4 MPa |
| CompressiveLoad | | ASTM D575 | 3.45 MPa |
| CompressiveLoad | | ASTM D575 | 56.5 MPa |
| CompressiveLoad | | ASTM D575 | 68.9 MPa |
| CompressiveLoad | | ASTM D575 | 13.8 MPa |
| CompressiveLoad | | ASTM D575 | 130 MPa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 700 MPa |
| Flexural modulus | | ISO 178 | 700 MPa |
| Taber abraser | | ISO 4649 | 65.0 mg |
| Taber abraser | | ASTM D1044 | 65.0 mg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 53 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 850 J/m |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTM D412 | 40.0 MPa |
| tensile strength | Yield | ISO 37 | 40.0 MPa |
| elongation | Break | ASTM D412 | 130 % |
| elongation | Break | ISO 37 | 130 % |
| tear strength | | ASTM D624 | 158 kN/m |
| tear strength | | ISO 34-1 | 160 kN/m |
| Shore hardness | | ASTM D2632 | 45 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 98.0 °C |
| Heat distortion temperature | | ISO 75-2/B | 98.0 °C |
| Heat distortion temperature | | ASTM D648 | 59.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 59.0 °C |
| brittle temperature | | ASTM D746 | <-68.0 °C |
| brittle temperature | | ISO 974 | <-68.0 °C |
| Glass Transition Temperature | | DMA | -35.0 °C |
| vicat | | ASTM D15253 | 139 °C |
| vicat | | ISO 306/50 | 139 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.