Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.23 g/cm³ |
| SpiralFlow | | 内部方法 | 87.0 cm |
| Shrinkage rate | | ISO294-4 | 0.70 % |
| Shrinkage rate | | ISO294-4 | 0.30 % |
| Water absorption rate | | ISO62 | 7.7to8.3 % |
| Humidity Absorption | | ISO1110 | 2.6to2.9 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 180 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| GlowWireFlammability Index | | IEC60695-2-12 | 650 °C |
| burning rate | | FMVSS302 | <100 mm/min |
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO1172 | 15 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 43 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 52 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 6.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 7.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 6100 MPa |
| Tensile stress | Break | ISO527-2/5 | 120 MPa |
| Tensile strain | Break | ISO527-2/5 | 3.0 % |
| Flexural modulus | | ISO178 | 5200 MPa |
| Bending stress | | ISO178 | 180 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+12 ohms |
| Volume resistivity | | IEC60093 | 1E+13 ohms·cm |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 205 °C |
| melting temperature | | DINEN11357-1 | 220 °C |
| | ISO75-2/B | 220 °C |
| TemperatureIndex | | IEC216 | 160to175 °C |
| TemperatureIndex | | IEC216 | 130to150 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.