TPU Multiuse Leostomer® LE-3160N
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 0.938 g/cm³ | |
| ISO1183 | 0.938 g/cm³ | ||
| melt mass-flow rate | ISO1133 | 1.5 g/10min | |
| ISO1133 | 1.5 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO868 | 60 | ||
| ISO868 | 60 |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | Break | ISO37 | 820 % |
| tear strength | ISO34-1 | 42 kN/m | |
| compression set | ISO815 | 41 % | |
| ISO815 | 35 % | ||
| Tensile stress | ISO37 | 1.70 MPa | |
| Yield | ISO37 | 15.0 MPa | |
| ISO37 | 1.70 MPa | ||
| Yield | ISO37 | 15.0 MPa | |
| elongation | Break | ISO37 | 820 % |
| tear strength | ISO34-1 | 42 kN/m | |
| compression set | ISO815 | 41 % | |
| ISO815 | 35 % |
| aging | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Change rate of tensile strength | ISO1817 | -6.0 % | |
| Changes in tensile stress during fracture | ISO1817 | 13 % | |
| Change rate of tensile strength | ISO1817 | -6.0 % | |
| Changes in tensile stress during fracture | ISO1817 | 13 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| brittle temperature | ISO974 | -60.0 °C | |
| ISO974 | -60.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.