Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | BS903 | 2.11 g/cm³ |
| Shrinkage rate | | | 0.50 % |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Viscosity | | | 350 Pa·s |
| Curing Time | | | <8.0 hr |
| surface drying time | | | 4.0 min |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 67 |
| tensile strength | | BS903 | 3.90 MPa |
| elongation | Break | BS903 | 100 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| VolumetricExpansion | | | 4.9E-04 cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | >1.0E+14 ohms·cm |
| dielectric strength | | ASTM D149 | >20 kV/mm |
| dielectric constant | | ASTM D150 | 4.90 |
| Dissipation Factor | | ASTM D150 | 9E-04 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | | 1.6E-04 cm/cm/°C |
| thermal conductivity | | | 2.3 W/m/K |
| Usage temperature | | | -50-220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.