PA66 Staramide RF006XXP EUROSTAR FRANCE

Properties:

Filler glass fiber reinforced material 30% filler by weight

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

Filler | glass fiber reinforced material | 30% | filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	7.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	8.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	55	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	75	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	8.0	kJ/m²
	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	8.0	kJ/m²
		Impact strength of cantilever beam gap	-20°C	ISO 180/1A	9.0	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	10	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	2.00mm	FMVSS302	6.0	mm/min
Burning rate	Burning rate	3.00mm	FMVSS302	2.0	mm/min
UL flame retardant rating	0.75mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	650	°C
Extreme Oxygen Index		ISO 4589-2	25	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	265	MPa
Bending modulus		ISO 178	9000	MPa
tensile strength	Break	ISO 527-2/5	175	MPa
Tensile strain	Break	ISO 527-2/5	3.0	%
Tensile modulus		ISO 527-2/1	9500	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	260	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	248	°C
Vicat softening temperature	--	ISO 306/B50	258	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	255	°C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	2.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	7.5E-05	cm/cm/°C
thermal conductivity		ISO 8302	0.33	W/m/K
RTI Elec		UL 746	65.0	°C
RTI Imp		UL 746	65.0	°C
RTI		UL 746	65.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.37	g/cm³
Shrinkage rate	MD	Internal Method	0.20to0.40	%
Water absorption rate	Saturation,23°C	ISO 62	4.5	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.3	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	>1.0E+16	ohms
Volume resistivity		IEC 60093	>1.0E+16	ohms·cm
Dielectric strength	3.20mm,in Oil	IEC 60243-1	19	kV/mm
Relative permittivity	50Hz	IEC 60250	3.40
Relative permittivity	Relative permittivity	60Hz	IEC 60250	3.40
Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 1
Relative permittivity	1MHz	IEC 60250	3.20
Dissipation factor	50Hz	IEC 60250	6.8E-03
	Dissipation factor	60Hz	IEC 60250	6.8E-03
	Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.015
Compared to the anti leakage trace index	--	IEC 60112	PLC 1
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	L-Sale	ISO 2039-2	113

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.